Home > Water Based Acrylic Resin >

Soft Film Forming Acrylic Emulsion For Water Based Varnish Polypropylene Felxo Inks

Product Categories

Water Based Acrylic Resin [180]
Solid Acrylic Resin [143]
Water Based Polyester Resin [20]
Polyethylene Wax Emulsion [82]
Water Based Alkyd Resin [31]
Solvent Based Acrylic Resin [60]
Water Based Epoxy Resin [44]
Mirror Effect Ink [46]
Epoxy Curing Agent [10]
Water Based Hydroxyl Acrylic Resin [34]
Water Based Peelable Resin [50]
High Hardness Floor Coatings [17]
Resins For Wood Coatings [27]
Water Based Industrial Coating Resins [29]

Xiamen WangQin Chemical Technology Co., Ltd.

Trust Seal

Verified Supplier

Credit Check

Supplier Assessment

Contact Now

Soft Film Forming Acrylic Emulsion For Water Based Varnish Polypropylene Felxo Inks

Name: Soft Film Forming Acrylic Emulsion For Water Based Varnish Polypropylene Felxo Inks
Brand: WeiLi Resin®
Price: 1 USD

Quality Soft Film Forming Acrylic Emulsion For Water Based Varnish Polypropylene Felxo Inks for sale

Brand Name : WeiLi Resin®

Model Number : WQ-2015

Certification : ISO9001

Place of Origin : China

MOQ : 5000KG

Price : Negotiable

Payment Terms : L/C, T/T

Supply Ability : 500t/month

Delivery Time : 14 work days

Packaging Details : 200kg/drum

Solid Content (%) : 49±1

Appearance : Milky white liquid

Acid Value : 50

Viscosity(mPa*s) : 1800-3000

PH(25℃) : 8.0-9.0

Tg(℃) : -23

MFFT(℃) : <0

Contact Now

Soft Film-Forming Acrylic Emulsion For Water Based Varnish For Polypropylene Felxo Inks

WQ-2015 acrylic emulsion is self-closslinking and excellent film-forming emulsion. WQ-2015 acrylic resin is specially designed for flexo & gravure ink and varnish, pigment dispersions, overprint varnishes, water based OPV. It promotes gloss, holdout, and resolubility in printing ink and overprint varnish formulations and can also be used to produce inorganic and organic pigment dispersions. WQ-2015 aqueous acrylic emulsion has excellent adhesion and good water resistance.

Key Features & Benefits

1, Self-closslinking and excellent film-forming

2, High adhesion

3, High resistance to water and oil

4, Excellent bond strength

Typical Physical Characteristics

Appearance	Milkywhite
Solid Content (%)	49±1
Acid Value	50
Viscosity(mPa*s)	1800-3000
PH(25℃)	8.0-9.0
Tg(℃)	-23
MFFT(℃)	<0

Recipes For Water Based Varnish For Polypropylene Felxo Inks

Water Based Varnish For PP (Polypropylene) (Flexography)

	No.	Raw Materials	%
	①	WQ-2015 (film-forming)	70.50
	②	WQ-2011 (non-film forming)	11.00
	③	WQ-2028 (acrylic resin solution)	12.00
	④	Wax emulsion	2.00
	⑤	Pure water	3.00
	⑥	DOWSIL™ 51 : Ethanol (1:1) *	1.00	Dow Corning
	⑦	Defoamer : Ethanol (1:1) *	0.50	MÜNZING AGITAN® 351
	Total		100.00
	Remark: 1. Premix ( ①＋②＋③), then add ④＋⑤+⑥, add the above materials and stir at the same time, at a constant speed, finally add ⑦. 2. *: DOWSIL™ 51 Additive diluted with Ethanol =1:1 AGITAN® 351 Defoamer diluted with Ethanol =1:1(Adjust the amount as per needs) 3. 4#cup: 15 seconds ± 5 PH value: 8.20 ± 0.5% 4. Final inks: - (Ajusting it accoring to needs) Yellow ink: varnish 65%+pigment paste 35% =100 Blue ink: varnish 65%+pigment paste 35% =100 Red ink: varnish 70%+pigment paste 30% =100 Black ink: varnish 70%+pigment paste 30% =100